99% Clear Liquid Vulcanizing Agent EPDM Crosslinking Agent Triallyl Isocyanurate Taic

Basic Info

Model NO.	TAIC-A
Kind	Crosslinking Agent
Appearance	Liquid
Transport Package	25kgs or 200kgs Per Drum
Specification	Clear Liquid
Trademark	SANJI
Origin	Hunan
Production Capacity	8000 Tons Per Year

Product Description

99% Clear Liquid Vulcanizing agent EPDM Crosslinking agent Triallyl isocyanurate TAIC

Formula: C12H15N3O3

Molecular Weight: 249.27

CAS#: 1025-15-6

Solubility:

Insoluble in water, slightly dissolved in alkane, and completely dissolved in aromatic hydrocarbon, alcohol, acetone, hydrocarbon halides, eyclopentene hydrocarbon.

Toxicity:

LD50 = 660mg/kg (Laboratory tested)

Package and Storage:

Packed in metal drum or plastic drum, Net weight is 200 or 25kg. or Packed in 25kg per kraft paper bag. Stored and transported as safe goods. Avoid high temperatures.

Specification:

Products	TAIC-A	TAIC-B	TAIC-P
Grade	Refined	Normal	Powder
Appearance	Clear liquid or crystal	Clear liquid or crystal	White powder
Hue(Pt-Co)	<50	<150	/
Active content	≥99.0%	≥95%	65%-67%, the other content is SiO2
Acid val.(mgKOH/g)	≤0.2	≤0.3	/
Melting point(ºC)	24-26	17-21	/
Viscosity(30ºC)	83+3cps	81+5cps	/
Spec.Gravity	1.15-1.17	1.10-1.17	/
Moisture(%)	<0.1	<0.1	<0.1
Bulk density(g/cm3)	/	/	0.38-0.48
PH	/	/	6.0-7.0

TAIC can be used in following industry :

1. PE/EVA : Radiation Crosslinking Sheet
2. PE/EVA Shoe,Mat,Toys,Handlegrip ect High-foaming products, TAIC is used as crosslinking agent assistant, It can
improve compression set. Tensile strength,Hardness,Resilience,Flexural modulus for Formula.
3. Wire & Cable of XLPE (Cross linked Polyethylene)
4. NBR (Notrile Butadiene Rubber)
5. Ethylene / propylene rubber is usually called EPDM
6. Fluorine rubber.
7. EVA film for solar battery encapsulation
8. Material for polymer alloy

TAIC is widely used as a coagent for peroxide crosslinking or radiation crosslinking of Chlorinated Polyethylene (CPE), EPDM, Fluroelaster and so on.

TAIC is availavle for linking by x-ray, y-ray electron or ultra violet ray radiation and the product polyolefines have the superior insolubility to solvents and the tensile strength at high temperature could be improved.

TAIC is effective modifier to heat resistance with increasing of crosslinking density for peroxide crosslinking denisty for peroxide crosslinking of CPE. Since TAIC acts as an acceptor of HCI which is envolved from CPE at crosslinking reaction and deterioriates its physical properties.

TAIC is the most effective coagent for crosslinking EVA.

TAIC preferably contributes to promote crosslinking rate and also to improve its heat resistance, compression set and abrasion resistance.